Influencia del tiempo de revenido en la resistencia al desgaste abrasivo, sobre un acero de bajo carbono y contenido de manganeso superior al 1%
Fecha
Autores
Autor corporativo
Título de la revista
ISSN de la revista
Título del volumen
Editor
Compartir
Director
Altmetric
Resumen
This document presents the study of abrasive wear performed on a low carbon steel and manganese content higher than 1%, after a quenching process, with variations of time and temperature. The process of characterization of the material used is initially described. Subsequently, the methodology and results obtained from the abrasive wear test performed under the ASTM G65 -04 Standard are presented. This test is performed prior to and after heat treatments carried out on the specimens. Next, hardness and microhardness tests are carried out on the specimens used, as well as determination of phase percentages and observation under SEM microscope. Finally, the conclusions obtained from this work are presented.
Descripción
Este documento presenta el estudio de desgaste abrasivo realizado sobre un acero de bajo carbono y contenido de manganeso superior al 1%, luego de un proceso de revenido, con variaciones de tiempo y temperatura. Se describe inicialmente el proceso de caracterización del material utilizado. Posteriormente se presenta la metodología y resultados obtenidos del ensayo de desgaste abrasivo ejecutados bajo la Norma ASTM G65 -04, lo anterior previa y posteriormente a los tratamientos térmicos realizados sobre las probetas. Seguidamente se realizan pruebas de dureza y microdureza sobre las probetas utilizadas, así como determinación de porcentajes de fase y observación bajo microscopio SEM. Presentando finalmente las conclusiones obtenidas del presente trabajo.
Palabras clave
Temple, Revenido, Desgaste, Abrasivo, Acero, Manganeso