Influencia de diferentes tratamientos térmicos y criogénico en la resistencia al impacto y dureza de un acero AISI SAE 5160
Fecha
Autor corporativo
Título de la revista
ISSN de la revista
Título del volumen
Editor
Compartir
Director
Altmetric
Resumen
This document shows the results of an experimental study that seeks to verify the effects of implementing cryogenics, as a thermal treatment combined with tempering and tempering in an AISI 5160 steel. Analyzing its changes in the microstructure of the material and its resistance to impact. Different dwell times of the test pieces are established at cryogenic temperatures of 12, 24 and 48 hours for each group of test pieces and control elements with hardening and tempering as points of comparison, the tempering is carried out at 760 ° C and the tempering at 300 °C.
Descripción
En este documento se muestran los resultados de un estudio experimental que busca verificar los efectos de implementar la criogenia como tratamiento térmico combinado con el temple y el revenido en un acero AISI 5160, analizando los cambios en la microestructura del material y en su resistencia al impacto. Se establecen diferentes tiempos de permanencia de las probetas a temperaturas criogénicas de 12, 24 y 48 horas para cada grupo de probetas y unos elementos de control con temple y revenido como puntos de comparación, el temple se realiza a 760°C y el revenido a 300° .
Palabras clave
Criogenia, 5160, Temple, Revenido, Impacto