Influencia del temple desde temperaturas intercríticas y particionamiento ¨q&p¨ en la resistencia a la fatiga de un acero sae 1045

Fecha

Autor corporativo

Título de la revista

ISSN de la revista

Título del volumen

Editor

Compartir

Altmetric

Resumen

Heat treatment of machined specimens for rotational bending fatigue testing of SAE 1045 steel. The quenching and partitioning heat treatment ¨Q&P¨ is carried out from intercritical temperatures at 760 °C and a partitioning step at 210 °C in an isothermal medium. of oil in the holding times of 60 min, 120 min and 180 min. After heat treatment, macrohardness, microhardness, rotational bending fatigue, scanning electron microscopy, dispersive energy X-ray spectroscopy and scanning electron microscopy were performed. The values obtained were related to each other and were compared with the results of previous studies of an SAE 1045 steel heat-treated by quenching and tempering ¨Q&T¨.

Descripción

Tratamiento térmico de probetas mecanizadas para ensayo de fatiga por flexión rotativa de un acero SAE 1045. El tratamiento térmico de temple y particionamiento ¨Q&P¨ se realiza desde temperaturas intercríticas a 760 °C y un paso de particionamiento a 210 °C en un medio isotérmico de aceite en los tiempos de sostenimiento de 60 min, 120 min y 180 min. Luego del tratamiento térmico se realizaron estudios de macrodureza, microdureza, fatiga por flexión rotativa, microcopia electrónica de barrido, espectroscopia de rayos X de energía dispersiva y Microscopía electrónica de barrido. Los valore obtenidos se relacionaron entre si y fueron comparados con resultados de estudios previos de un acero SAE 1045 tratado térmicamente mediante temple y revenido ¨Q&T¨.

Palabras clave

Temple, Particionamiento, Fatiga

Materias

Ingeniería Mecánica -- Tesis y disertaciones académicas , Tratamiento térmico , Fatiga por flexión rotativa , Acero SAE 1045 , Microestructura