Estudio de aplicabilidad del óxido de zinc como modificador del cemento asfáltico en una mezcla densa en caliente
Fecha
Autor corporativo
Título de la revista
ISSN de la revista
Título del volumen
Editor
Compartir
Altmetric
Resumen
In this study, the applicability of zinc oxide as a modifier for asphalt cement (AC 60-70) and its behavior in a hot mix asphalt of type MDC-19 were evaluated. Penetration, softening point, viscosity, and ductility tests were conducted on the modified asphalt binder (1, 2, 3, 4, 5, 7.5, and 10% ZnO by weight of AC) and the unmodified binder. The temperature and mixing time of AC with ZnO were primarily considered with environmental criteria. The MDC-19 mixture design, manufactured with and without binder modification, was performed using the Marshall method. Characterization tests, including indirect tension, Cantabro, resilient modulus, and permanent deformation, were conducted on the asphalt mixtures.
Descripción
En el presente estudio se evaluó la aplicabilidad del óxido de zinc (ZnO) como modificador de un cemento asfáltico (CA 60-70) y su comportamiento en una mezcla asfáltica en caliente de tipo MDC-19. Sobre el ligante asfáltico modificado (1, 2, 3, 4, 5, 7.5 y 10% de ZnO con respecto a la masa del CA) y sin modificar se llevaron a cabo ensayos de penetración, punto de ablandamiento, viscosidad y ductilidad. La temperatura y tiempo de mezcla del CA con el ZnO se realizó teniendo en cuenta principalmente criterios ambientales. El diseño de la mezcla MDC-19, fabricada con y sin modificación del ligante, se realizó por medio del método Marshall. Sobre las mezclas asfálticas se realizaron ensayos de caracterización de tensión indirecta, cántabro, módulo resiliente y deformación permanente.
Palabras clave
Óxido de zinc, Asfalto modificado, Mezclas asfálticas modificadas, Mezcla densa en caliente