Ensayo Jominy desde temperaturas intercriticas en aceros 4140 y 8620
Fecha
Autor corporativo
Título de la revista
ISSN de la revista
Título del volumen
Editor
Universidad Distrital Francisco José de Caldas
Compartir
Director
Altmetric
Resumen
This project aims to analyze the microstructure behavior of 4140 and 8620 steels after heat treatment. Specimens of each steel will be manufactured according to ASTM A255 using the Jominy method, and then heat treated with intercritical temperatures. Hardness data and microstructure formation will be verified for each specimen. To observe the microstructure formation of each specimen and steel in detail, a metallographic procedure will be performed along the length of each specimen. Finally, any changes found along the length of each specimen, changes that may occur after applying each intercritical temperature, will be observed and documented.
Descripción
En el presente proyecto, se contempla analizar el comportamiento de la microestructura en los aceros 4140 y 8620 posterior a un tratamiento térmico. Donde se fabricarán probetas de cada acero según la norma ASTM A255 aplicado a el método Jominy, a las cuales se realizará tratamientos térmicos con temperaturas intercríticas. Se realizará el proceso de verificación de datos de dureza y formación de microestructuras de cada una de las probetas.
Para llegar a observar de manera detallada la formación de microestructura de cada probeta y acero, se realizará el procedimiento metalográfico a lo largo de cada probeta. Para finalmente, observar y documentar los cambios que se encuentren a lo largo de cada probeta, cambios que se puedan generar luego de aplicar cada temperatura intercrítica.
Palabras clave
Temple Jominy, Aceros AISI/SAE 4140 y 8620, Microestructura, Tratamiento térmico intercrítico, Dureza