Análisis de la Resistencia al Desgaste Abrasivo de un Acero AISI-SAE 1020 Templado a una Temperatura de 800°C y Revenido a Diferentes Temperaturas
Fecha
Autor corporativo
Título de la revista
ISSN de la revista
Título del volumen
Editor
Compartir
Director
Altmetric
Resumen
The present Project has as purpose to analyze the resistance to the abrasive wear and the micro-structural comportment from a steel AISI-SAE 1020. These were considered taking the material in delivery estate, hardened process to an intercritical temperature of 800°C and tempering to different temperatures but in the same period of time.This process tries to figure out the steel reactions AISI-SAE 1020 against the abrasive erosion, having into account the different hardness values which appear during the previous process. Tests mass loss was conducted, optical microscopy and electronic (MEB) scanning, besides, hardness tests. This kind of steel was chosen because of its high consumption in the industry and its low carbon content
Descripción
El proyecto que se presenta, tiene como fin el análisis de la resistencia al desgaste abrasivo y comportamiento micro estructural, de un acero AISI-SAE 1020, este fue realizado tomando el material en estado de entrega. Ejecutándole procesos de temple a temperatura intercritica de 800°C y revenidos a diferentes temperaturas, pero en el mismo intervalo de tiempo.Con esto se busca determinar el comportamiento del acero AISI-SAE 1020 frente al desgaste abrasivo, teniendo en cuenta los diferentes valores de dureza que se presentan durante los procesos anteriores. Se llevaron a cabo pruebas de porcentaje de pérdida de masa, microscopia óptica y de barrido electrónico (MEB), además, de ensayos de dureza. Se eligió este acero por su alto consumo en la industria y su bajo contenido de carbono.
Palabras clave
Desgaste Abrasivo, Acero de Bajo Carbono, Pérdida de Masa, Microestructura