Influencia del tiempo de revenido en la resistencia al desgaste abrasivo de un Acero AISI 1020 templado desde temperaturas intercríticas seguido de un tratamiento criogénico
Fecha
Autor corporativo
Título de la revista
ISSN de la revista
Título del volumen
Editor
Compartir
Director
Altmetric
Resumen
In this study the effect on resistance to abrasive wear of three heat treatments is analyzed in a steel SAE 1020. The study of the material was carried out from its base state or delivery, hardened to intercritical temperatures using two cooling ways, followed by a cryogenic treatment and finally tempered at different times. The results show that there is a minimal increase in abrasive wear resistance by performing hardening at the highest temperature or A3 using water as the cooling way and in any tempering time.
Descripción
En este trabajo se analiza el efecto sobre la resistencia al desgaste abrasivo de tres tratamientos térmicos en un acero SAE 1020. El estudio sobre el material, se llevó a cabo desde su estado base o de entrega, con un temple a temperaturas intercríticas empleando dos medios de enfriamiento, seguido de un tratamiento criogénico y finalmente revenido a diferentes tiempos. Los resultados muestran que hay un mínimo aumento en la resistencia al desgaste abrasivo al realizar un temple a la mayor temperatura o A3 empleando agua como método de enfriamiento y en cualquier tiempo de revenido.
Palabras clave
Temperaturas intercríticas, Criogenia, Desgaste abrasivo, Tratamientos térmicos