Influencia de la temperatura de revenido en la energía absorbida para un acero 1045 tratado térmicamente desde temperaturas intercríticas
Fecha
Autor corporativo
Título de la revista
ISSN de la revista
Título del volumen
Editor
Compartir
Director
Altmetric
Resumen
This paper determined the behavior of the hardness and energy absorbed on the impact of a SAE 1045 steel by being quenching from intercritical temperatures and tempering above the bainitic transformation temperature with times of 10, 20 and 30 minutes. In addition to This was done the micrographs by means of optical microscopy and scanning electron microscopy, concluding that For the realized temperings it is found that the energy absorbed to the impact increases significantly with increasing the time of tempering, this is best observed in the tempering done to The tempered specimens from temperatures close to the upper intercritical (AC3)
Descripción
Este trabajo determino el comportamiento de las propiedades de dureza y energía absorbida al impacto de un acero SAE 1045 al ser templado desde temperaturas intercríticas y ser revenido por encima de la temperatura de transformación bainítica con tiempos de 10, 20, y 30 minutos, además de esto se realizaron las tomas de micrografías por medio de microscopia óptica y microscopia electrónica de barrido, concluyendo que Para los revenidos realizados se encuentra que la energía absorbida al impacto aumenta significativamente al incrementar el tiempo de revenido, esto se observa mejor en los revenidos realizados a las probetas templadas desde temperaturas cercanas a la intercrítica superior (AC3)
Palabras clave
Acero, Charpy, Impacto, Intercritica, Temperatura, Microscopia