Toledo Bueno, Carlos AugustoRevelo Cuarán, Edwin Alexander2022-06-062022-06-062021-03-29http://hdl.handle.net/11349/29260Objetivo: Analizar morfológicamente por medio microscopía electrónica de barrido (SEM), tableros aglomerados elaborados con cascarilla de arroz e hidropul 400 y tableros elaborados a partir de las virutas de madera y pegamento. Metodología: Se tomaron dos muestras por probeta de 7.3 x 3.6 x 1.5 cm en las secciones externas e internas por cada uno de los paneles a analizar, se realizaron recubrimientos de capa fina de grafito a cada una de ellas; por medio del microscopio electrónico de barrido se realizaron tomas micrográficas en rangos de 50x a 2000x. Resultados: Se evidencio que el panel fabricado con cascarilla de arroz, presentaba afectaciones en su estructura interna, debido a la porosidad, a las capas cerosas de su recubrimiento, a la alta presencia de sílice y la presencia de agua dentro del adhesivo, mostrando irregularidades en adherencia entre partículas y bajas propiedades mecánicas. Conclusiones: Aunque el panel a base de cascarilla de arroz estudiado no obtuvo las propiedades adecuadas estructurales, tiene grandes aplicaciones para el diseño de interiores, además por estructura porosa se consideran su potencial como material absorbente del sonido. De igual forma se puede mejorar el material al hacer un pretratamiento de la cascarilla o combinar con diferentes fibras vegetales más leñosas como desperdicios de madera, bambú, fibra de coco entre otrosObjective: To morphologically analyze by means of scanning electron microscopy (SEM), agglomerated boards made from rice husk and Hidropul 400 and boards made from wood fibers and glue. Methodology: By each test piece of 7.3 x 3.6 x 1.5 cm, two samples were taken from the external and internal sections on each one of the boards to be analyzed, thin-layer graphite coatings were made to each one of them; by means of the scanning electron microscope, micrographic shots were obtained in ranges from 50x to 2000x. Results: It was evidenced that the panel made from rice husk had breakages in its internal structure, due to porosity, the waxy layers of its coating, the high presence of silica and the presence of water inside the adhesive, showing irregularities in adhesion between particles and low mechanical properties. Conclusions: Although the studied rice husk panel did not obtain adequate structural properties, it has great applications for interior design. In addition, due to its porous structure its potential as sound-absorbing material is considered. In the same way, the material can be improved by pre-treating the husk or combining it with other, more woody plant fibers such as wood waste, bamboo, coconut fiber, among others.pdfspaAtribución-NoComercial-SinDerivadas 4.0 Internacionalhttp://creativecommons.org/licenses/by-nc-nd/4.0/SEMAglomeradoTablero de PartículasHomogeneizaciónArrozCascarillaIngeniería Industrial - Tesis y disertaciones académicasResiduos agrícolasCascarilla de arrozConstrucciones prefabricadasMateriales de construcciónConstrucción industrializadainfo:eu-repo/semantics/restrictedAccessSEMAgglomerateRiceHuskHomogenizationParticlesboardProducción AcadémicaRestringido (Solo Referencia)